Calorimetric analyses on aged Al-4Cu-0.5Mg-0.9Si-0.8Mn alloy (AA2014 grade) (Articolo in rivista)
- Type
- Label
- Calorimetric analyses on aged Al-4Cu-0.5Mg-0.9Si-0.8Mn alloy (AA2014 grade) (Articolo in rivista) (literal)
- Anno
- 2007-01-01T00:00:00+01:00 (literal)
- Http://www.cnr.it/ontology/cnr/pubblicazioni.owl#doi
- 10.1007/s10973-006-7836-3 (literal)
- Alternative label
- Http://www.cnr.it/ontology/cnr/pubblicazioni.owl#autori
- P. Bassani; E. Gariboldi; G. Vimercati (literal)
- Pagina inizio
- Pagina fine
- Http://www.cnr.it/ontology/cnr/pubblicazioni.owl#numeroVolume
- Rivista
- Note
- ISI Web of Science (WOS) (literal)
- Http://www.cnr.it/ontology/cnr/pubblicazioni.owl#affiliazioni
- 1National Research Council Institute for Energetics and Interphases, CNR-IENI Unit of Lecco, Corso P. Sposi
29-23900 Lecco, Italy
2Politecnico di Milano, Dipartimento di Meccanica, Via La Masa, 34, 20156 Milano, Italy (literal)
- Titolo
- Calorimetric analyses on aged Al-4Cu-0.5Mg-0.9Si-0.8Mn alloy (AA2014 grade) (literal)
- Abstract
- An Al-4.4Cu-0.5Mg-0.9Si-0.8Mn alloy (IADS 2014 grade) in the solution annealed and peak aged condition was exposed
at 170°C for relatively long times (up to about 1800 h) in order to check the stability of the alloy. The investigated aging temperature
was in the frame of a research on the long-term mechanical behaviour of such alloy. Microstructure evolution was monitored
via calorimetric analyses, metallographic inspections and hardness measurements. Further, X-ray analyses were carried out on selected
samples. The attention was focused on differential scanning calorimetry performed at different scanning rates, with the aim
of evaluating the kinetics of the precipitation phenomena. Notwithstanding the wide industrial diffusion of this alloy, literature survey
showed that there is not a consensus view on the precipitation sequences and on calorimetric peak identification.
The present results show the progressive evolution of calorimetric peaks, corresponding to that of strengthening particles towards
more stable phases, proved by the disappearance of exothermic peaks. Activation energy from Kissinger kinetic analysis in
the case of aged samples provided scattered values that could be reasonably attributed to an overlapping of transformation peaks.
Moreover, in these samples transformations partially occurred before DSC scans, providing non-constant transformation fraction at
signal peak temperatures and resulting in different activation energies. (literal)
- Prodotto di
- Autore CNR
- Insieme di parole chiave
Incoming links:
- Autore CNR di
- Prodotto
- Http://www.cnr.it/ontology/cnr/pubblicazioni.owl#rivistaDi
- Insieme di parole chiave di