A Template Metal-Organic Chemical Vapour Deposition Route to the Fabrication of Free Standing Co3O4 nanotbes arrays (Articolo in rivista)

Type

• Articolo in rivista (Classe)
• Prodotto della ricerca (Classe)

Label

• A Template Metal-Organic Chemical Vapour Deposition Route to the Fabrication of Free Standing Co3O4 nanotbes arrays (Articolo in rivista) (literal)

Anno

• 2009-01-01T00:00:00+01:00 (literal)

Http://www.cnr.it/ontology/cnr/pubblicazioni.owl#doi

• 10.1166/nnl.2009.1020 (literal)

Alternative label

• L. M. S. Perdicaro, R. G. Toro, M. E. Frgala'. G. Malandrino, R. Lo Nigro, C. Bongiorno, M. Losurdo, M. M. Giangregorio, G. Bruno (2009)
  A Template Metal-Organic Chemical Vapour Deposition Route to the Fabrication of Free Standing Co3O4 nanotbes arrays
  in Nanoscience and nanotechnology letters (Print)
  (literal)

Http://www.cnr.it/ontology/cnr/pubblicazioni.owl#autori

• L. M. S. Perdicaro, R. G. Toro, M. E. Frgala'. G. Malandrino, R. Lo Nigro, C. Bongiorno, M. Losurdo, M. M. Giangregorio, G. Bruno (literal)

Pagina inizio

• 87 (literal)

Pagina fine

• 92 (literal)

Http://www.cnr.it/ontology/cnr/pubblicazioni.owl#numeroVolume

• 1 (literal)

Rivista

• Nanoscience and nanotechnology letters (Rivista)

Http://www.cnr.it/ontology/cnr/pubblicazioni.owl#pagineTotali

• 6 (literal)

Note

• ISI Web of Science (WOS) (literal)

Http://www.cnr.it/ontology/cnr/pubblicazioni.owl#affiliazioni

• Dipartimento di scineze Chimiche, Università di Catania Istituto per la Microelettronica e Microsistemi Istituto di metodologie inorganiche e del Plasmi (literal)

Titolo

• A Template Metal-Organic Chemical Vapour Deposition Route to the Fabrication of Free Standing Co3O4 nanotbes arrays (literal)

Abstract

• Large area Co3O4 nanotube arrays were fabricated through a metal-organic chemical vapour deposition (MOCVD) template route using the Co(tta)2 ·tmeda (Htta=2 thenoyl-trifluoroacetone, tmeda= N,N,N?,N?-tetramethylethylendiamine) as precursor and anodic aluminum oxide (AAO) as template. The scanning electron microscopy (SEM) and transmission electron microscopy (TEM) indicated a very uniform distribution of nanotubes forming an array on a very large scale of the order of mm2. X-ray diffraction (XRD) pattern shows the formation of the Co3O4 cubic spinel phase. The electron diffraction confirmed the crystalline Co3O4 phase even after removal of the AAO template. Spectroscopic ellipsometry was used to measure the optical properties of nanotubes and to discuss the effect of the nanostructure with respect to the optical properties of Co3O4 thin films. (literal)

Prodotto di

• Materiali multifunzionali, e innovativi per componenti integrati (MD.P05.003.002) (Modulo)
• Institute for microelectronics and microsystems (IMM) (Istituto)

Autore CNR

• CORRADO BONGIORNO (Unità di personale interno)
• ROBERTA GRAZIA TORO (Unità di personale interno)
• GIOVANNI BRUNO (Unità di personale interno)
• MARIA LOSURDO (Unità di personale interno)
• RAFFAELLA LO NIGRO (Unità di personale interno)

Insieme di parole chiave

• Keywords of "A Template Metal-Organic Chemical Vapour Deposition Route to the Fabrication of Free Standing Co3O4 nanotbes arrays" (Insieme di parole chiave)

Incoming links:

Autore CNR di

• GIOVANNI BRUNO (Unità di personale interno)
• MARIA LOSURDO (Unità di personale interno)
• RAFFAELLA LO NIGRO (Unità di personale interno)
• CORRADO BONGIORNO (Unità di personale interno)
• ROBERTA GRAZIA TORO (Unità di personale interno)

Prodotto

• Institute for microelectronics and microsystems (IMM) (Istituto)
• Materiali multifunzionali, e innovativi per componenti integrati (MD.P05.003.002) (Modulo)

Http://www.cnr.it/ontology/cnr/pubblicazioni.owl#rivistaDi

• Nanoscience and nanotechnology letters (Rivista)

Insieme di parole chiave di

• Keywords of "A Template Metal-Organic Chemical Vapour Deposition Route to the Fabrication of Free Standing Co3O4 nanotbes arrays" (Insieme di parole chiave)