A simple method for the synthesis of silicon carbide nanorods (Articolo in rivista)

Type
Label
  • A simple method for the synthesis of silicon carbide nanorods (Articolo in rivista) (literal)
Anno
  • 2002-01-01T00:00:00+01:00 (literal)
Alternative label
  • Kholmanov I.N., Kharlamov A., Barborini E., Lenardi C., Li Bassi A., Bottani C.E., Ducati C., Maffi S., Kirillova N.V., Milani P. (2002)
    A simple method for the synthesis of silicon carbide nanorods
    in Journal of nanoscience and nanotechnology (Print)
    (literal)
Http://www.cnr.it/ontology/cnr/pubblicazioni.owl#autori
  • Kholmanov I.N., Kharlamov A., Barborini E., Lenardi C., Li Bassi A., Bottani C.E., Ducati C., Maffi S., Kirillova N.V., Milani P. (literal)
Pagina inizio
  • 453 (literal)
Pagina fine
  • 456 (literal)
Http://www.cnr.it/ontology/cnr/pubblicazioni.owl#numeroVolume
  • 2 (literal)
Rivista
Note
  • ISI Web of Science (WOS) (literal)
Http://www.cnr.it/ontology/cnr/pubblicazioni.owl#affiliazioni
  • INFM Dipartimento di Fisica, Università di Milano, Via Celoria 16, 20133 Milano, Italy Thermophysics Department, Uzbek Academy of Science, Katartal str,28, 700135 Tashkent, Uzbekistan Institute of Materials Science, National Academy of Sciences of Ukraine, Krzhyzhanovski str. 3,252142 Kiev, Ukraine INFM Dipartimento di Ingegneria Nucleare (CESNEF), Politecnico di Milano, Via Ponzio 34/3, 20133 Milano, Italy Department of Engineering, University of Cambridge, CB2 1PZ, Cambridge, UK CESPEL-CNR, Dipartimento di Chimica Fisica Applicata, Politecnico di Milano, Via Mancinelli 7, 20131 Milano, Italy T. Shevchenko Kyiv National University, 64 Volodymyrska Vil., 01033 Kyiv, Ukraine (literal)
Titolo
  • A simple method for the synthesis of silicon carbide nanorods (literal)
Abstract
  • SiC nanorods were synthesized by a reaction at a temperature of 1200°C, under an argon gas atmosphere, from silicon and amorphous carbon powder mixed by ball milling. The reaction products, which contain SiC nanorods, were characterized by X-ray diffraction and micro-Raman spectroscopy. The synthesized nanorods are more than 1 micron long with a mean diameter of about 10-30 nm. The nanorods possess a well-defined crystaline structure with a thin layer of amorphous SiO2 on the surface. Raman shifts of SiC nanorods and the role of structural defects are discussed. (literal)