Influence of Ce3+/Ce4+ ratio on phase stability and residual stress field in ceria-yttria stabilized zirconia plasma-sprayed coatings (Articolo in rivista)
- Type
- Label
- Influence of Ce3+/Ce4+ ratio on phase stability and residual stress field in ceria-yttria stabilized zirconia plasma-sprayed coatings (Articolo in rivista) (literal)
- Anno
- 1992-01-01T00:00:00+01:00 (literal)
- Http://www.cnr.it/ontology/cnr/pubblicazioni.owl#doi
- 10.1007/BF00541628 (literal)
- Alternative label
R. Dal Maschio, P. Scardi, L. Lutterotti, G.M. Ingo (1992)
Influence of Ce3+/Ce4+ ratio on phase stability and residual stress field in ceria-yttria stabilized zirconia plasma-sprayed coatings
in Journal of materials science
(literal)
- Http://www.cnr.it/ontology/cnr/pubblicazioni.owl#autori
- R. Dal Maschio, P. Scardi, L. Lutterotti, G.M. Ingo (literal)
- Pagina inizio
- Pagina fine
- Http://www.cnr.it/ontology/cnr/pubblicazioni.owl#numeroVolume
- Rivista
- Http://www.cnr.it/ontology/cnr/pubblicazioni.owl#pagineTotali
- Http://www.cnr.it/ontology/cnr/pubblicazioni.owl#numeroFascicolo
- Note
- ISI Web of Science (WOS) (literal)
- Http://www.cnr.it/ontology/cnr/pubblicazioni.owl#affiliazioni
- R. Dal Maschio, P. Scardi, L. Lutterotti, G.M. Ingo [2]
[1] UNIVERITA' DI TRENTO, DIPARTIMENTO INGEGNERIA DEI MATERIALI,I-38050 TRENT,ITALY.
[2] CNR, ISTITUTO DI TEORIA & STRUTTURA ELETTRONICA, AREA DELLA RICERCA DI ROMA, CP 10, 00016 MONTEROTONDO STAZIONE, ROME, ITALY (literal)
- Titolo
- Influence of Ce3+/Ce4+ ratio on phase stability and residual stress field in ceria-yttria stabilized zirconia plasma-sprayed coatings (literal)
- Abstract
- CeO2-Y2O3 stabilized zirconia plasma-sprayed coatings have been produced by two different procedures based on different cooling rates. A high cooling rate (HCR) induced the contemporary presence of CeO2 and Ce2O3, while cooling in calm air (LCR) induced the presence of only CeO2. After subjecting the HCR coating, detached from the substrate, to an air thermal treatment, which oxidizes Ce2O3 to CeO2, a lower thermal expansion coefficient was measured than in the LCR material, and shrinkage was also observed. This behaviour is explained by the phase composition changes induced by the oxidation of ceria. (literal)
- Prodotto di
- Autore CNR
- Insieme di parole chiave
Incoming links:
- Prodotto
- Autore CNR di
- Http://www.cnr.it/ontology/cnr/pubblicazioni.owl#rivistaDi
- Insieme di parole chiave di