XPS STUDIES ON THE SURFACE THERMAL MODIFICATIONS OF TIN OXIDES (Abstract in rivista)

Type

• Prodotto della ricerca (Classe)
• Abstract in rivista (Classe)

Label

• XPS STUDIES ON THE SURFACE THERMAL MODIFICATIONS OF TIN OXIDES (Abstract in rivista) (literal)

Anno

• 1988-01-01T00:00:00+01:00 (literal)

Http://www.cnr.it/ontology/cnr/pubblicazioni.owl#doi

• 10.1002/sia.740120720 (literal)

Alternative label

• E. PAPARAZZO, G. FIERRO, G.M. INGO, N. ZACCHETTI (1988)
  XPS STUDIES ON THE SURFACE THERMAL MODIFICATIONS OF TIN OXIDES
  
  (literal)

Http://www.cnr.it/ontology/cnr/pubblicazioni.owl#autori

• E. PAPARAZZO, G. FIERRO, G.M. INGO, N. ZACCHETTI (literal)

Pagina inizio

• 438 (literal)

Pagina fine

• 439 (literal)

Http://www.cnr.it/ontology/cnr/pubblicazioni.owl#numeroVolume

• 12 (literal)

Rivista

• SIA. Surface and interface analysis (Rivista)

Http://www.cnr.it/ontology/cnr/pubblicazioni.owl#pagineTotali

• 2 (literal)

Http://www.cnr.it/ontology/cnr/pubblicazioni.owl#numeroFascicolo

• 1-12 (literal)

Note

• ISI Web of Science (WOS) (literal)

Http://www.cnr.it/ontology/cnr/pubblicazioni.owl#affiliazioni

• E. PAPARAZZO (1), G. FIERRO (2), G.M. INGO (2), N. ZACCHETTI (2) (1) CNR,IST TEORIA STRUTTURA ELETTRON & COMPORTAMENTO SPETTROCHIM COMPOSTI COORDINAZ,F-00016 MONTEROTONDO,ITALY. (2) Centro Sviluppo Materiali, Castel Romano, Rome Italy (literal)

Titolo

• XPS STUDIES ON THE SURFACE THERMAL MODIFICATIONS OF TIN OXIDES (literal)

Abstract

• The authors have studied surface decompositions induced by high-temperature treatments (up to 825 K) at the surface of SnO2 oxide and SnO oxide, the latter being chosen for the purposes of comparison. XPS spectroscopy was used to monitor such modifications. They find that Sn0 forms at the surface when SnO2 and SnO are annealed to 825 K, and non-stoichiometric tin oxide species become apparent in the sub-surface region of the former. Insurgence of Sn metal at the surface of thermally treated tin oxides could be related to the results of recent work by J.W. Erickson and S. Semancik, who reported a significant increase of surface electrical conductivity in SnO2 annealed to 800 K, and higher temperatures. (literal)

Editore

• Heyden (Editore)

Prodotto di

• Institute of structure of matter (ISM) (Istituto)
• Istituto per lo studio dei materiali nanostrutturati (ISMN) (Istituto)
• Sintesi e crescita di film e superfici nanostrutturate (PM.P05.004.002) (Modulo)

Autore CNR

• ERNESTO PAPARAZZO (Unità di personale interno)
• GABRIEL MARIA INGO (Unità di personale interno)
• GIUSEPPE FIERRO (Unità di personale interno)

Incoming links:

Autore CNR di

• ERNESTO PAPARAZZO (Unità di personale interno)
• GIUSEPPE FIERRO (Unità di personale interno)
• GABRIEL MARIA INGO (Unità di personale interno)

Prodotto

• Institute of structure of matter (ISM) (Istituto)
• Istituto per lo studio dei materiali nanostrutturati (ISMN) (Istituto)
• Sintesi e crescita di film e superfici nanostrutturate (PM.P05.004.002) (Modulo)

Http://www.cnr.it/ontology/cnr/pubblicazioni.owl#rivistaDi

• SIA. Surface and interface analysis (Rivista)

Editore di

• Heyden (Editore)