Synthesis of TiO2 rutile nanoparticles by PLA in solution (Articolo in rivista)

Type
Label
  • Synthesis of TiO2 rutile nanoparticles by PLA in solution (Articolo in rivista) (literal)
Anno
  • 2012-01-01T00:00:00+01:00 (literal)
Http://www.cnr.it/ontology/cnr/pubblicazioni.owl#doi
  • 10.1016/j.apsusc.2011.10.057 (literal)
Alternative label
  • V. Caratto a,b, M. Ferrettia, b, L. Settia, b (2012)
    Synthesis of TiO2 rutile nanoparticles by PLA in solution
    in Applied surface science
    (literal)
Http://www.cnr.it/ontology/cnr/pubblicazioni.owl#autori
  • V. Caratto a,b, M. Ferrettia, b, L. Settia, b (literal)
Pagina inizio
  • 2393 (literal)
Pagina fine
  • 2396 (literal)
Http://www.cnr.it/ontology/cnr/pubblicazioni.owl#numeroVolume
  • 258 (literal)
Rivista
Http://www.cnr.it/ontology/cnr/pubblicazioni.owl#pagineTotali
  • 4 (literal)
Http://www.cnr.it/ontology/cnr/pubblicazioni.owl#numeroFascicolo
  • 7 (literal)
Http://www.cnr.it/ontology/cnr/pubblicazioni.owl#affiliazioni
  • a Dipartimento di Chimica e Chimica Industriale, Università di Genova, Via Dodecaneso 31, 16146 Genova, Italy b CNR-SPIN, Corso Perrone 24, 16152 Genova, Italy (literal)
Titolo
  • Synthesis of TiO2 rutile nanoparticles by PLA in solution (literal)
Abstract
  • This paper describes the synthesis of TiO2 nanoparticles by laser ablation in solution synthesis (Lasis). The laser excimer beam passes through a focusing lens and it is sent to the reaction chamber. The frequency used during the synthesis was 20 Hz, intensity 26 kV The metal ablated by the laser beam undergoes an oxidation process resulting from the reaction with water. We obtain TiO2 nanoparticles with average size of 6.5 nm, crystallized in the rutile structure. The crystallographic and morphological structure was studied by transmission electron microscopy (literal)
Prodotto di
Autore CNR
Insieme di parole chiave

Incoming links:


Autore CNR di
Prodotto
Http://www.cnr.it/ontology/cnr/pubblicazioni.owl#rivistaDi
Insieme di parole chiave di
data.CNR.it