Morphology and molecular orientation in sexithiophene and N,N '-bis (n-octyl)-dicyanoperylenediimide heterostructures (Articolo in rivista)

Type

• Articolo in rivista (Classe)
• Prodotto della ricerca (Classe)

Label

• Morphology and molecular orientation in sexithiophene and N,N '-bis (n-octyl)-dicyanoperylenediimide heterostructures (Articolo in rivista) (literal)

Anno

• 2012-01-01T00:00:00+01:00 (literal)

Alternative label

• Tkachenko, V1; Di Girolamo, FV1; Chiarella, F2; Cassinese, A1; Abbate, G1 (2012)
  Morphology and molecular orientation in sexithiophene and N,N '-bis (n-octyl)-dicyanoperylenediimide heterostructures
  in Thin solid films (Print)
  (literal)

Http://www.cnr.it/ontology/cnr/pubblicazioni.owl#autori

• Tkachenko, V1; Di Girolamo, FV1; Chiarella, F2; Cassinese, A1; Abbate, G1 (literal)

Pagina inizio

• 2390 (literal)

Pagina fine

• 2394 (literal)

Http://www.cnr.it/ontology/cnr/pubblicazioni.owl#numeroVolume

• 520 (literal)

Rivista

• Thin solid films (Rivista)

Http://www.cnr.it/ontology/cnr/pubblicazioni.owl#pagineTotali

• 5 (literal)

Http://www.cnr.it/ontology/cnr/pubblicazioni.owl#numeroFascicolo

• 7 (literal)

Http://www.cnr.it/ontology/cnr/pubblicazioni.owl#affiliazioni

• 1Università di Napoli Federico 2, CNR SPIN, I-80126 Napoli 2Università degli Studi di Salerno, CNR SPIN I-84084 Fisciano Salerno (literal)

Titolo

• Morphology and molecular orientation in sexithiophene and N,N '-bis (n-octyl)-dicyanoperylenediimide heterostructures (literal)

Abstract

• We report on the growth mode of N,N'-bis (n-octyl)-dicyanoperylenediimide (PDI-8CN(2)) on sexithiophene (T6) thin films, studied with different structural, morphological and optical techniques. We aim to individuate the most favorable conditions for the realization of heterostructure devices. The crystalline quality was established by X-ray patterns and Atomic Force Microscopy (AFM) images, and found to be generally high. The anisotropic optical constants extracted from ellipsometry measurements shed light on the mean molecular orientation in the PDI-8CN(2) film. AFM images evidence two different growth modes: at T6 thickness less than 2 monolayers (ML), the growth of PDI-8CN(2) on T6 is favored with respect to SiO2, while, at higher thickness (2-6 ML), the situation is reversed. An optimum T6 underlayer thickness of approximately 1 ML provides the best quality of PDI-8CN(2) layer corresponding to the highest island dimension, the highest molecular order parameter, and the lowest roughness. Spectrum broadening was observed for extinction coefficient of PDI-8CN(2) in the heterostructures, as compared with a sole material film, and explained by two effects: increase in molecular disorder and formation of charge transfer complexes. (literal)

Prodotto di

• Metodologie innovative per lo studio ed il controllo delle proprietà (opto)elettroniche di materiali e dispositivi multifunzionali (MD.P04.026.003) (Modulo)
• Realizzazione e studio di materiali con forti correlazioni di spin, carica ed orbitale (MD.P04.025.001) (Modulo)
• Materiali e dispositivi innovativi per l'elettronica, la plasmonica e la fotonica (MD.P04.026.004) (Modulo)

Autore CNR

• GIANCARLO ABBATE (Unità di personale esterno)
• VOLODYMYR TKACHENKO (Unità di personale interno)
• FABIO CHIARELLA (Unità di personale interno)
• ANTONIO CASSINESE (Persona)

Incoming links:

Autore CNR di

• GIANCARLO ABBATE (Unità di personale esterno)
• ANTONIO CASSINESE (Persona)
• VOLODYMYR TKACHENKO (Unità di personale interno)
• FABIO CHIARELLA (Unità di personale interno)

Prodotto

• Realizzazione e studio di materiali con forti correlazioni di spin, carica ed orbitale (MD.P04.025.001) (Modulo)
• Materiali e dispositivi innovativi per l'elettronica, la plasmonica e la fotonica (MD.P04.026.004) (Modulo)
• Metodologie innovative per lo studio ed il controllo delle proprietà (opto)elettroniche di materiali e dispositivi multifunzionali (MD.P04.026.003) (Modulo)

Http://www.cnr.it/ontology/cnr/pubblicazioni.owl#rivistaDi

• Thin solid films (Rivista)