Vibrational and electrical properties of hexagonal La2O3 films (Articolo in rivista)

Type
Label
  • Vibrational and electrical properties of hexagonal La2O3 films (Articolo in rivista) (literal)
Anno
  • 2007-01-01T00:00:00+01:00 (literal)
Http://www.cnr.it/ontology/cnr/pubblicazioni.owl#doi
  • 10.1063/1.2779108 (literal)
Alternative label
  • Scarel, G; Debernardi, A; Tsoutsou, D; Spiga, S; Capelli, SC; Lamagna, L; Volkos, SN; Alia, M; Fanciulli, M (2007)
    Vibrational and electrical properties of hexagonal La2O3 films
    in Applied physics letters
    (literal)
Http://www.cnr.it/ontology/cnr/pubblicazioni.owl#autori
  • Scarel, G; Debernardi, A; Tsoutsou, D; Spiga, S; Capelli, SC; Lamagna, L; Volkos, SN; Alia, M; Fanciulli, M (literal)
Pagina inizio
  • 102901 (literal)
Http://www.cnr.it/ontology/cnr/pubblicazioni.owl#numeroVolume
  • 91 (literal)
Rivista
Note
  • ISI Web of Science (WOS) (literal)
Http://www.cnr.it/ontology/cnr/pubblicazioni.owl#affiliazioni
  • INFM, MDM Natl Lab, CNR, I-20041 Agrate Brianza, Italy (literal)
Titolo
  • Vibrational and electrical properties of hexagonal La2O3 films (literal)
Abstract
  • La2O3 films are obtained by annealing in vacuum La(OH)(3) layers produced upon air exposure of La2O3 layers grown using atomic layer deposition. Sample thickness determines whether hexagonal or cubic La2O3 form. The observed infrared active phonon mode with minimum frequency for hexagonal La2O3 films is located at 198 cm(-1), in good agreement with the first principles calculations, and at a lower frequency than the corresponding mode for cubic La2O3 is at 235 cm(-1). Accordingly, electrical measurements reveal a dielectric constant around 27 for hexagonal La2O3 films, significantly higher than the one around 17 derived for cubic La2O3 layers. (C) 2007 American Institute of Physics. (literal)
Prodotto di
Autore CNR
Insieme di parole chiave

Incoming links:


Autore CNR di
Prodotto
Http://www.cnr.it/ontology/cnr/pubblicazioni.owl#rivistaDi
Insieme di parole chiave di
data.CNR.it