Characterization and comparison of 1% at Yb-doped Lu2O3 and Sc2O3 ceramics as laser gain media (Articolo in rivista)

Type

• Prodotto della ricerca (Classe)
• Articolo in rivista (Classe)

Label

• Characterization and comparison of 1% at Yb-doped Lu2O3 and Sc2O3 ceramics as laser gain media (Articolo in rivista) (literal)

Anno

• 2012-01-01T00:00:00+01:00 (literal)

Http://www.cnr.it/ontology/cnr/pubblicazioni.owl#doi

• 10.1134/S1054660X12120237 (literal)

Alternative label

• Angela Pirri, Guido Toci, Matteo Vannini (2012)
  Characterization and comparison of 1% at Yb-doped Lu2O3 and Sc2O3 ceramics as laser gain media
  in Laser physics
  (literal)

Http://www.cnr.it/ontology/cnr/pubblicazioni.owl#autori

• Angela Pirri, Guido Toci, Matteo Vannini (literal)

Pagina inizio

• 1851 (literal)

Pagina fine

• 1855 (literal)

Http://www.cnr.it/ontology/cnr/pubblicazioni.owl#url

• http://link.springer.com/article/10.1134/S1054660X12120237 (literal)

Http://www.cnr.it/ontology/cnr/pubblicazioni.owl#numeroVolume

• 22 (literal)

Rivista

• Laser physics (Rivista)

Http://www.cnr.it/ontology/cnr/pubblicazioni.owl#pagineTotali

• 5 (literal)

Http://www.cnr.it/ontology/cnr/pubblicazioni.owl#numeroFascicolo

• 12 (literal)

Http://www.cnr.it/ontology/cnr/pubblicazioni.owl#affiliazioni

• IFAC-CNR (literal)

Titolo

• Characterization and comparison of 1% at Yb-doped Lu2O3 and Sc2O3 ceramics as laser gain media (literal)

Abstract

• We present the first laser oscillation achieved on Yb?doped Sc2O3 and Lu2O3 ceramics with a level of doping as low as 1 at %, under quasi?continuous wave pumping at 968 nm. Ceramic samples reached com? parable performances in terms of tunability ranges, which exceeds 41 nm, and laser output powers. In partic? ular, with the former sample emitting at 1040.5 nm we measured a maximum output power of 2.2 W with a corresponding slope efficiency of ? = 59%. The latter medium delivered 1.8 W with a slope of ? = 45% at 1032.5 nm while at 1078 nm we measured 1.5 W with ? = 34%. Finally, we report the measured level of the Amplified Spontaneous Emission (ASE) for both samples, which was found to be less than 0.1 mW at the maximum pump power. (literal)

Prodotto di

• Institute of applied physics \"Nello Carrara\" (IFAC) (Istituto)
• Dispositivi e materiali laser innovativi e metodi spettroscopici avanzati (MD.P03.002.001) (Modulo)
• Dispositivi e materiali Laser innovativi e sistemi Laser per il telerilevamento (MD.P03.038.002) (Modulo)

Autore CNR

• ANGELA PIRRI (Unità di personale interno)
• GUIDO TOCI (Unità di personale interno)
• MATTEO VANNINI (Persona)

Insieme di parole chiave

• Keywords of "Characterization and comparison of 1% at Yb-doped Lu2O3 and Sc2O3 ceramics as laser gain media" (Insieme di parole chiave)

Incoming links:

Autore CNR di

• MATTEO VANNINI (Persona)
• GUIDO TOCI (Unità di personale interno)
• ANGELA PIRRI (Unità di personale interno)

Prodotto

• Institute of applied physics \"Nello Carrara\" (IFAC) (Istituto)
• Dispositivi e materiali Laser innovativi e sistemi Laser per il telerilevamento (MD.P03.038.002) (Modulo)
• Dispositivi e materiali laser innovativi e metodi spettroscopici avanzati (MD.P03.002.001) (Modulo)

Http://www.cnr.it/ontology/cnr/pubblicazioni.owl#rivistaDi

• Laser physics (Rivista)

Insieme di parole chiave di

• Keywords of "Characterization and comparison of 1% at Yb-doped Lu2O3 and Sc2O3 ceramics as laser gain media" (Insieme di parole chiave)