The HER in alkaline media on Pt-modified three-dimensional Ni cathodes (Articolo in rivista)

Type
Label
  • The HER in alkaline media on Pt-modified three-dimensional Ni cathodes (Articolo in rivista) (literal)
Anno
  • 2012-01-01T00:00:00+01:00 (literal)
Http://www.cnr.it/ontology/cnr/pubblicazioni.owl#doi
  • 10.1016/j.ijhydene.2012.04.100 (literal)
Alternative label
  • Fiameni S.; Herraiz-Cardona I.; Musiani M.; Pérez-Herranz V.; Vázquez-Gómez L.; Verlato E. (2012)
    The HER in alkaline media on Pt-modified three-dimensional Ni cathodes
    in International journal of hydrogen energy; Elsevier Ltd, Oxford (Regno Unito)
    (literal)
Http://www.cnr.it/ontology/cnr/pubblicazioni.owl#autori
  • Fiameni S.; Herraiz-Cardona I.; Musiani M.; Pérez-Herranz V.; Vázquez-Gómez L.; Verlato E. (literal)
Pagina inizio
  • 10507 (literal)
Pagina fine
  • 10516 (literal)
Http://www.cnr.it/ontology/cnr/pubblicazioni.owl#url
  • http://www.sciencedirect.com/science/article/pii/S0360319912009937 (literal)
Http://www.cnr.it/ontology/cnr/pubblicazioni.owl#numeroVolume
  • 37 (literal)
Rivista
Http://www.cnr.it/ontology/cnr/pubblicazioni.owl#pagineTotali
  • 9 (literal)
Http://www.cnr.it/ontology/cnr/pubblicazioni.owl#numeroFascicolo
  • 14 (literal)
Note
  • ISI Web of Science (WOS) (literal)
  • Scopu (literal)
Http://www.cnr.it/ontology/cnr/pubblicazioni.owl#affiliazioni
  • 1,3,5,6 : IENI CNR, Corso Stati Uniti 4, 35127 Padova, Italy / 2,4 : Ingeniería Electroquímica y Corrosión (IEC), Departamento de Ingeniería Química y Nuclear, Universitat Politècnica de València, Camino de Vera s/n, 46022 Valencia, Spain (literal)
Titolo
  • The HER in alkaline media on Pt-modified three-dimensional Ni cathodes (literal)
Abstract
  • Electrodeposited porous Ni layers and commercial Ni foams were submitted to spontaneous deposition of Pt, achieved by immersing the Ni substrates in H2PtCl6 solutions, at open circuit, to produce Pt-modified 3D Ni electrodes. When using Ni foams, the immersion was prolonged until the whole amount of H2PtCl6 in the solution had reacted. Such an approach, which granted an easy control of the Pt loading, could not be used for Ni electrodeposits, since they underwent significant corrosion. The true Pt surface area was determined by measuring, for each electrode, the hydrogen desorption charge according to methods described in the literature. The ratios between Pt surface area and Pt loading were higher for Ni foam electrodes than for porous Ni electrodeposits. Both kinds of Pt-modified Ni electrodes were used as cathodes for hydrogen evolution in 1 M KOH. Cathodes with Pt loading below 0.5 mg cm?2 (referred to geometric surface area) evolved hydrogen at ?100 mA cm?2 with a ?75 mV overpotential. The better activity of foam electrodes as compared to electrodeposits, especially at low Pt loading, was mainly due to their higher Pt surface area per unit Pt mass. (literal)
Editore
Prodotto di
Autore CNR
Insieme di parole chiave

Incoming links:


Prodotto
Autore CNR di
Http://www.cnr.it/ontology/cnr/pubblicazioni.owl#rivistaDi
Editore di
Insieme di parole chiave di
data.CNR.it