Wet Chemical Method for Making Graphene-like Films from Carbon Black (Articolo in rivista)
- Type
- Label
- Wet Chemical Method for Making Graphene-like Films from Carbon Black (Articolo in rivista) (literal)
- Anno
- 2012-01-01T00:00:00+01:00 (literal)
- Http://www.cnr.it/ontology/cnr/pubblicazioni.owl#doi
- 10.1021/am301197q (literal)
- Alternative label
M. Alfè; V. Gargiulo; R. Di Capua; F. Chiarella; J-Nl Rouzaud; A. Vergara; A. Ciajolo (2012)
Wet Chemical Method for Making Graphene-like Films from Carbon Black
in ACS applied materials & interfaces (Online); ACS, American chemical society, Washington, DC (Stati Uniti d'America)
(literal)
- Http://www.cnr.it/ontology/cnr/pubblicazioni.owl#autori
- M. Alfè; V. Gargiulo; R. Di Capua; F. Chiarella; J-Nl Rouzaud; A. Vergara; A. Ciajolo (literal)
- Pagina inizio
- Pagina fine
- Http://www.cnr.it/ontology/cnr/pubblicazioni.owl#numeroVolume
- Rivista
- Http://www.cnr.it/ontology/cnr/pubblicazioni.owl#pagineTotali
- Http://www.cnr.it/ontology/cnr/pubblicazioni.owl#numeroFascicolo
- Note
- Scopus (literal)
- ISI Web of Science (WOS) (literal)
- Http://www.cnr.it/ontology/cnr/pubblicazioni.owl#affiliazioni
- Istituto di Ricerche sulla Combustione (IRC)-CNR, P.le Tecchio, 80, 80125 Napoli, Italy
SPIN-CNR UOS Napoli, via Cintia, I-80126, Napoli, Italy.
Dipartimento S.pe.S., Universita' del Molise, Via De Sanctis, I-86100, Campobasso, Italy
SPIN-CNR UOS Salerno, Via Ponte don Melillo, I-84084, Fisciano (SA), Italy
Laboratoire de Geologie, Ecole Normale Superieure, 24 Rue Lhomond, 75231 Paris Cedex 05, France
Dipartimento di Scienze Chimiche, Complesso Universitario di Monte Sant'Angelo, Via Cintia, 21, 80126 Napoli, Italy (literal)
- Titolo
- Wet Chemical Method for Making Graphene-like Films from Carbon Black (literal)
- Abstract
- Reduction of strongly oxidized carbon black by hydrazine hydrate yields water-insoluble graphene-like sheets that undergo to self-assembling in thin film on surfaces after drying. The height of a drop-casted graphene-like film was determined by atomic force microscopy (AFM) to be around 20 nm, corresponding to approximately 25 graphene-like layers. The oxidized carbon black and the corresponding reduced form were carefully characterized. (literal)
- Editore
- Prodotto di
- Autore CNR
- Insieme di parole chiave
Incoming links:
- Autore CNR di
- Prodotto
- Editore di
- Http://www.cnr.it/ontology/cnr/pubblicazioni.owl#rivistaDi
- Insieme di parole chiave di