Liquid crystalline elastomers based on diglycidyl terminated rigid monomers and aliphatic acids. Part 1. Synthesis and characterization (Articolo in rivista)
- Type
- Label
- Liquid crystalline elastomers based on diglycidyl terminated rigid monomers and aliphatic acids. Part 1. Synthesis and characterization (Articolo in rivista) (literal)
- Anno
- 2005-01-01T00:00:00+01:00 (literal)
- Alternative label
Ambrogi, V.; Giamberini, M.; Cerruti, P.; Pucci, P.; Menna, N.; Mascolo, R.; Carfagna (2005)
Liquid crystalline elastomers based on diglycidyl terminated rigid monomers and aliphatic acids. Part 1. Synthesis and characterization
in Polymer (Guildford)
(literal)
- Http://www.cnr.it/ontology/cnr/pubblicazioni.owl#autori
- Ambrogi, V.; Giamberini, M.; Cerruti, P.; Pucci, P.; Menna, N.; Mascolo, R.; Carfagna (literal)
- Pagina inizio
- Pagina fine
- Http://www.cnr.it/ontology/cnr/pubblicazioni.owl#numeroVolume
- Rivista
- Http://www.cnr.it/ontology/cnr/pubblicazioni.owl#note
- No. Citazione=7;
Autocitazione=3;
Motore utilizzato per le citazioni=Google Scholar. (literal)
- Note
- ISI Web of Science (WOS) (literal)
- Http://www.cnr.it/ontology/cnr/pubblicazioni.owl#affiliazioni
- CNR, Università di Napoli Federico II. (literal)
- Titolo
- Liquid crystalline elastomers based on diglycidyl terminated rigid monomers and aliphatic acids. Part 1. Synthesis and characterization (literal)
- Abstract
- Liquid crystalline elastomers (LCEs) were prepared by reacting rigid-rod mesogenic epoxy monomers with aliphatic diacids of variable length. The influence of acid and nature of epoxy monomer on the mechanism of network growth was investigated through DSC, FT-IR, MALDI, 1H and 13C NMR and rheological experiments. Depending on the nature of epoxy monomer, different mechanisms of network growth occurred, which were responsible for the formation of elastomers with different extent of branching.
Clearing temperatures, enthalpies and entropies, and the nature of mesophases were also analyzed through DSC and X-ray diffraction, carried out on unstrained elastomers. It was found that both the rigid-rod mesogens and the aliphatic portions of carboxylic acids contribute to stabilize the mesophase. Moreover, upon stretching, all the LCEs exhibited the polydomain-to-monodomain transition, which is typical of this class of materials. (literal)