Evidence of direct correlation between out-of-plane lattice parameter and metal-insulator transition temperature in oxygen-depleted manganite thin films (Articolo in rivista)
- Type
- Label
- Evidence of direct correlation between out-of-plane lattice parameter and metal-insulator transition temperature in oxygen-depleted manganite thin films (Articolo in rivista) (literal)
- Anno
- 2012-01-01T00:00:00+01:00 (literal)
- Http://www.cnr.it/ontology/cnr/pubblicazioni.owl#doi
- 10.1063/1.3676268 (literal)
- Alternative label
P. Orgiani; A. Yu. Petrov; R. Ciancio; A. Galdi; L. Maritato and B. A. Davidson (2012)
Evidence of direct correlation between out-of-plane lattice parameter and metal-insulator transition temperature in oxygen-depleted manganite thin films
in Applied physics letters; American Institute Of Physics (AIP), Melville (Stati Uniti d'America)
(literal)
- Http://www.cnr.it/ontology/cnr/pubblicazioni.owl#autori
- P. Orgiani; A. Yu. Petrov; R. Ciancio; A. Galdi; L. Maritato and B. A. Davidson (literal)
- Pagina inizio
- Pagina fine
- Http://www.cnr.it/ontology/cnr/pubblicazioni.owl#url
- http://apl.aip.org/resource/1/applab/v100/i4/p042404_s1 (literal)
- Http://www.cnr.it/ontology/cnr/pubblicazioni.owl#numeroVolume
- Rivista
- Http://www.cnr.it/ontology/cnr/pubblicazioni.owl#pagineTotali
- Http://www.cnr.it/ontology/cnr/pubblicazioni.owl#numeroFascicolo
- Note
- ISI Web of Science (WOS) (literal)
- Scopu (literal)
- Http://www.cnr.it/ontology/cnr/pubblicazioni.owl#affiliazioni
- CNR-SPIN and University of Salerno, I-84084 Fisciano (SA), Italy
CNR-IOM TASC, Area Science Park, I-34149 Basovizza (TS), Italy (literal)
- Titolo
- Evidence of direct correlation between out-of-plane lattice parameter and metal-insulator transition temperature in oxygen-depleted manganite thin films (literal)
- Abstract
- We report on the role of oxygen content alone on structural and transport properties of La0.65Sr0.35MnO3?d (LSMO) thin films. Identical films were deposited side-by-side during a single deposition run and subsequently post-annealed separately in vacuum to systematically vary the oxygen content. All films remained coherently strained to the SrTiO3 substrate, with no broadening of rocking curve widths after post-anneal. As oxygen content decreases, the LSMO unit cell expands while the metal-insulator transition temperature TMI decreases. A linear correlation between the out-of-plane lattice parameter and the metal-insulator transition temperature was observed. (literal)
- Editore
- Prodotto di
- Autore CNR
- Insieme di parole chiave
Incoming links:
- Autore CNR di
- Prodotto
- Http://www.cnr.it/ontology/cnr/pubblicazioni.owl#rivistaDi
- Editore di
- Insieme di parole chiave di