Characterization of plasma -coated wool fabrics (Articolo in rivista)

Type

• Articolo in rivista (Classe)
• Prodotto della ricerca (Classe)

Label

• Characterization of plasma -coated wool fabrics (Articolo in rivista) (literal)

Anno

• 2009-01-01T00:00:00+01:00 (literal)

Http://www.cnr.it/ontology/cnr/pubblicazioni.owl#doi

• 10.1177/0040517508097516 (literal)

Alternative label

• Mossotti R.; Lopardo G.; Innocenti R.; Mazzuchetti G.; Rombaldoni F.; Montarsolo A.; Vassallo E. (2009)
  Characterization of plasma -coated wool fabrics
  in Textile research journal
  (literal)

Http://www.cnr.it/ontology/cnr/pubblicazioni.owl#autori

• Mossotti R.; Lopardo G.; Innocenti R.; Mazzuchetti G.; Rombaldoni F.; Montarsolo A.; Vassallo E. (literal)

Pagina inizio

• 853 (literal)

Pagina fine

• 861 (literal)

Http://www.cnr.it/ontology/cnr/pubblicazioni.owl#numeroVolume

• 79 (literal)

Rivista

• Textile research journal (Rivista)

Http://www.cnr.it/ontology/cnr/pubblicazioni.owl#numeroFascicolo

• 9 (literal)

Note

• ISI Web of Science (WOS) (literal)

Http://www.cnr.it/ontology/cnr/pubblicazioni.owl#affiliazioni

• Mossotti R., Lopardo G., Innocenti R., Mazzuchetti G., Rombaldoni F., Montarsolo A. CNR ISMAC Vassallo E. CNR Istituto Fisica del Plasma (literal)

Titolo

• Characterization of plasma -coated wool fabrics (literal)

Abstract

• (Si : O(x) : C(y) : H(z)) thin films were deposited on knitted wool fabrics by plasma-enhanced chemical-vapor deposition using hexamethyldisiloxane as a monomer and argon and oxygen as feed gases in low-pressure equipment. Fourier transform infrared spectroscopy and X-ray photoelectron spectroscopy analyses confirmed the presence of the siloxane coating. The pilling tendency of treated samples was investigated for different deposition powers, ranging from 30 to 50 W A reduction on pill formation was observed for all treated samples. A silicone-based wet chemical treatment was taken as the reference method for pilling reduction and plasma treatments were compared with it. The pilling grade of treated fabrics was also tested after washing and the results confirmed a good pilling behavior of plasma-treated fabrics. Changes were observed in the bursting resistance of plasma-treated wool samples compared with untreated ones, while no significant differences were found in the whiteness index. (literal)

Prodotto di

• Materiali tessili, Tecnofibre e Processi industriali per la filiera tessile (SP.P01.031.001) (Modulo)
• Sviluppo di Impianti e Strumentazione per i Plasmi e per la Fusione Termonucleare (ET.P05.002.001) (Modulo)
• Istituto per lo studio delle macromolecole (ISMAC) (Istituto)
• Istituto di fisica del plasma \"Piero Caldirola\" (IFP) (Istituto)

Autore CNR

• GIORGIO MAZZUCHETTI (Unità di personale interno)
• GIUSEPPINA LOPARDO (Persona)
• RICCARDO INNOCENTI (Persona)
• ALESSIO MONTARSOLO (Persona)
• FABIO ROMBALDONI (Unità di personale esterno)
• RAFFAELLA MOSSOTTI (Unità di personale interno)
• ESPEDITO VASSALLO (Unità di personale interno)

Incoming links:

Prodotto

• Istituto di fisica del plasma \"Piero Caldirola\" (IFP) (Istituto)
• Istituto per lo studio delle macromolecole (ISMAC) (Istituto)
• Materiali tessili, Tecnofibre e Processi industriali per la filiera tessile (SP.P01.031.001) (Modulo)
• Sviluppo di Impianti e Strumentazione per i Plasmi e per la Fusione Termonucleare (ET.P05.002.001) (Modulo)

Autore CNR di

• RICCARDO INNOCENTI (Persona)
• ESPEDITO VASSALLO (Unità di personale interno)
• RAFFAELLA MOSSOTTI (Unità di personale interno)
• GIORGIO MAZZUCHETTI (Unità di personale interno)
• FABIO ROMBALDONI (Unità di personale esterno)
• ALESSIO MONTARSOLO (Persona)
• GIUSEPPINA LOPARDO (Persona)

Http://www.cnr.it/ontology/cnr/pubblicazioni.owl#rivistaDi

• Textile research journal (Rivista)