Formation of short and long chain branches during the free radical functionalization of polyamide 6 in the melt (Articolo in rivista)

Type

• Prodotto della ricerca (Classe)
• Articolo in rivista (Classe)

Label

• Formation of short and long chain branches during the free radical functionalization of polyamide 6 in the melt (Articolo in rivista) (literal)

Anno

• 2006-01-01T00:00:00+01:00 (literal)

Http://www.cnr.it/ontology/cnr/pubblicazioni.owl#doi

• 10.1021/ma051893o (literal)

Alternative label

• Coltelli M .B., Angiuli M., Passaglia E., Castelvetro V., Ciardelli F., (2006)
  Formation of short and long chain branches during the free radical functionalization of polyamide 6 in the melt
  in Macromolecules (Print)
  (literal)

Http://www.cnr.it/ontology/cnr/pubblicazioni.owl#autori

• Coltelli M .B., Angiuli M., Passaglia E., Castelvetro V., Ciardelli F., (literal)

Pagina inizio

• 2153 (literal)

Pagina fine

• 2161 (literal)

Http://www.cnr.it/ontology/cnr/pubblicazioni.owl#numeroVolume

• 39 (literal)

Rivista

• Macromolecules (Rivista)

Note

• Scopu (literal)
• ISI Web of Science (WOS) (literal)

Http://www.cnr.it/ontology/cnr/pubblicazioni.owl#affiliazioni

• (1) INFM, PolyLab, I-56126 Pisa, Italy (2) IPCF - CNR (3) CNR, ICCOM,Sez Pisa, I-56126 Pisa, Italy (4) Univ Pisa, Dipartimento Chim & Chim Ind (literal)

Titolo

• Formation of short and long chain branches during the free radical functionalization of polyamide 6 in the melt (literal)

Abstract

• Polyamide 6 (PA6) was treated in the melt at 230 degrees C in a discontinuous mixer with diethyl maleate (DEM) and dicumyl peroxide (DCP). The grafting of DEM to PA6 chains was investigated by H-1 NMR analysis, and it reached easily up to 4.5 mol %. The grafted diethyl succinate groups (DES) can successively react with terminal ammo groups of different polyamide macromolecules, thus yielding branched polyamide macromolecules. The average degree of branching, determined by titration analysis, is about one per macromolecule under the used experimental conditions and can be improved by further blending with PA6. Thermal analysis of branched PA6 showed lower melting and crystallization temperatures than those of simply processed linear PA6. Blends of unmodified and functionalized polyamide showed a higher viscosity and a more effective shear thinning behavior than the simply processed linear PA6. Experimental evidence was discussed, and a possible reaction mechanism was proposed. (literal)

Prodotto di

• Istituto di chimica dei composti organo metallici (ICCOM) (Istituto)
• Processi di post-modifica e miscelazione reattiva per la preparazione di sistemi macromolecolari multifasici, nanostrutturati e funzionali (PM.P02.005.006) (Modulo)
• Sviluppo e applicazioni di metodologie preparative di materiali polimerici funzionali nanostrutturati in processi di reactive blending (PM.P03.015.005) (Modulo)

Autore CNR

• FRANCESCO CIARDELLI (Persona)
• ELISA PASSAGLIA (Persona)

Insieme di parole chiave

• Keywords of "Formation of short and long chain branches during the free radical functionalization of polyamide 6 in the melt" (Insieme di parole chiave)

Incoming links:

Prodotto

• Istituto di chimica dei composti organo metallici (ICCOM) (Istituto)
• Processi di post-modifica e miscelazione reattiva per la preparazione di sistemi macromolecolari multifasici, nanostrutturati e funzionali (PM.P02.005.006) (Modulo)
• Sviluppo e applicazioni di metodologie preparative di materiali polimerici funzionali nanostrutturati in processi di reactive blending (PM.P03.015.005) (Modulo)

Autore CNR di

• ELISA PASSAGLIA (Persona)
• FRANCESCO CIARDELLI (Persona)

Http://www.cnr.it/ontology/cnr/pubblicazioni.owl#rivistaDi

• Macromolecules (Rivista)

Insieme di parole chiave di

• Keywords of "Formation of short and long chain branches during the free radical functionalization of polyamide 6 in the melt" (Insieme di parole chiave)