Fatigue crack growth in poycrystalline IN 718 superalloy (Articolo in rivista)

Type

• Articolo in rivista (Classe)
• Prodotto della ricerca (Classe)

Label

• Fatigue crack growth in poycrystalline IN 718 superalloy (Articolo in rivista) (literal)

Anno

• 2003-01-01T00:00:00+01:00 (literal)

Alternative label

• Osinkolu G.A., Onofrio G., Marchionni M. (2003)
  Fatigue crack growth in poycrystalline IN 718 superalloy
  
  (literal)

Http://www.cnr.it/ontology/cnr/pubblicazioni.owl#autori

• Osinkolu G.A., Onofrio G., Marchionni M. (literal)

Pagina inizio

• 425 (literal)

Pagina fine

• 433 (literal)

Http://www.cnr.it/ontology/cnr/pubblicazioni.owl#altreInformazioni

• Memoria pubblicata su Material Scince and Engineering Vol A356 pp 425-433 (literal)

Http://www.cnr.it/ontology/cnr/pubblicazioni.owl#numeroVolume

• A356 (literal)

Http://www.cnr.it/ontology/cnr/pubblicazioni.owl#descrizioneSinteticaDelProdotto

• Sono stati studiati gli effetti della temperatura e della dimensione del grano microstrutturale sulla propagazione di cricca per fatica della superlega di Nichel policristallina IN718. Un modello di previsione di vita basato sulla legge di Paris e che utilizza due parametri descrive accuratamente il fenomeno della propagazione di cricca anche in considerazione della frattura intergranulare indotta dalla diffusione dell'ossigeno. (literal)

Note

• ISI Web of Science (WOS) (literal)

Http://www.cnr.it/ontology/cnr/pubblicazioni.owl#affiliazioni

• 1 CERD Università di Ile-Ife Nigeria 2, 3 CNR IENI sezione di Milano (literal)

Titolo

• Fatigue crack growth in poycrystalline IN 718 superalloy (literal)

Abstract

• The fatigue crack growth rate (FCGR) of a polycrystalline IN 718 superalloy was investigated at 650°C for two different grain sizes using single notch tension (SENT) specimens. In air the FCGR is insensitive to the grain size in the mixed time-cycle dependent regime and the oxidation-induced intergranular fracture controls the crack growth rate. When a hold time is applied the coarse microstructure shows a lower resistance to crack propagation both in air and in vacuum. A two parameter Paris equation was found to describe the relationship between the loading frequency and the crack growth rate, which provides valuable insight into the oxygen-induced intergranular fracture mechanisms operating at elevated temperature. (literal)

Prodotto di

• Materiali strutturali innovativi per l'energetica (ET.P06.005.001) (Modulo)
• Institute of Condensed Matter Chemistry and Energy Technologies (ICMATE) (Istituto)

Autore CNR

• MASSIMO MARCHIONNI (Persona)
• GIOVANNI ONOFRIO (Persona)

Insieme di parole chiave

• Keywords of "Fatigue crack growth in poycrystalline IN 718 superalloy" (Insieme di parole chiave)

Incoming links:

Autore CNR di

• GIOVANNI ONOFRIO (Persona)
• MASSIMO MARCHIONNI (Persona)

Prodotto

• Institute of Condensed Matter Chemistry and Energy Technologies (ICMATE) (Istituto)
• Materiali strutturali innovativi per l'energetica (ET.P06.005.001) (Modulo)

Insieme di parole chiave di

• Keywords of "Fatigue crack growth in poycrystalline IN 718 superalloy" (Insieme di parole chiave)