http://www.cnr.it/ontology/cnr/individuo/prodotto/ID16867
Crystal-to-crystal phase transition and CO2 adsorption properties of polymeric magnesium formate (Articolo in rivista)
- Type
- Label
- Crystal-to-crystal phase transition and CO2 adsorption properties of polymeric magnesium formate (Articolo in rivista) (literal)
- Anno
- 2008-01-01T00:00:00+01:00 (literal)
- Http://www.cnr.it/ontology/cnr/pubblicazioni.owl#doi
- 10.1021/cg800181q (literal)
- Alternative label
Rossin, Andrea; Ienco, Andrea; Costantino, Ferdinando; Montini, Tiziano; Di Credico, Barbara; Caporali, Maria; Gonsalvi, Luca; Fornasiero, Paolo; Peruzzini, Maurizio (2008)
Crystal-to-crystal phase transition and CO2 adsorption properties of polymeric magnesium formate
in Crystal growth & design; ACS, American chemical society, Washington, DC (Stati Uniti d'America)
(literal)
- Http://www.cnr.it/ontology/cnr/pubblicazioni.owl#autori
- Rossin, Andrea; Ienco, Andrea; Costantino, Ferdinando; Montini, Tiziano; Di Credico, Barbara; Caporali, Maria; Gonsalvi, Luca; Fornasiero, Paolo; Peruzzini, Maurizio (literal)
- Pagina inizio
- Pagina fine
- Http://www.cnr.it/ontology/cnr/pubblicazioni.owl#numeroVolume
- Rivista
- Note
- ISI Web of Science (WOS) (literal)
- Http://www.cnr.it/ontology/cnr/pubblicazioni.owl#affiliazioni
- ICCOM-CNR; Universita' di Trieste; Universita' di Perugia (literal)
- Titolo
- Crystal-to-crystal phase transition and CO2 adsorption properties of polymeric magnesium formate (literal)
- Abstract
- The solvothermal reaction of magnesium(II) salts with formic acid in N,N-dimethylformamide/H2O at 140 °C for
24 h afforded two different polymeric magnesium(II) formates, depending on the relative DMF/H2O content. A trigonal (space group R3j c) anhydrous phase Mg(HCOO)2(HCOOH) ? (CH3)2NH (1) is formed under \"dilute\" conditions, while the orthorhombic (space group Pbca) dihydrate Mg(HCOO)2 ·2H2O (2) is the main product when the water content is higher. When 2 is dehydrated at 300 °C and subsequently exposed to water vapors, a quasi-reversible phase transition was observed, leading to a different polymorph of the same species (2a, monoclinic, space group P21/c). The process was entirely followed by X-ray powder diffraction (XRPD)
at variable temperatures, and the same XRPD technique was used for structure solution and refinement of compound 2a. Finally, CO2 adsorption isotherms at ambient temperature were recorded for (preactivated) 2, in order to test it as greenhouse gas storage material. A (promising) maximum value of 1.32 wt% CO2 is stored under these conditions, but the plateau in the adsorption curve was not reached because of the higher carbon dioxide pressures required. (literal)
- Editore
- Prodotto di
- Autore CNR
- Insieme di parole chiave
Incoming links:
- Prodotto
- Autore CNR di
- Http://www.cnr.it/ontology/cnr/pubblicazioni.owl#rivistaDi
- Editore di
- Insieme di parole chiave di